Magnetic and dielectric studies of barium hexaferrite (BaFe 12 O 19 ) ceramic synthesized by chemical route

Abstract

Barium hexaferrite BaFe 12 O 19 (BHF) ceramic was synthesized by chemical route on sintering at 1050 °C for 12 h. The synthesized material was characterized by XRD, SEM, AFM and TEM analysis. Metal oxide stretching frequencies corresponding to Fe-O, Ba-O, and Fe-O-Fe bands are confirmed by FTIR studies. The hexagonal nature of the BHF ceramic was confirmed by TEM analysis and Rietveld refinement with space group P6 3 /mmc. The particle size observed by TEM is 175 nm. The root means square and average roughness were found to be 61.048 nm and 44.025 nm respectively. The M-T and M-H hysteresis loop indicates temperature dependent ferromagnetic behavior of BHF ceramic. The temperature and frequency dependent dielectric properties were explained by Maxwell-Wagner theory. The value of dielectric constant (ε′) for BHF ceramic was found to be 22× 10 3 at 100 Hz and 483 K. © 2018, Springer Science+Business Media, LLC, part of Springer Nature.