High temperature impedance spectroscopy of barium stannate, BaSnO3

Abstract

Polycrystalline powder of BaSnO3 was prepared at 1300 °C using a high-temperature solid-state reaction technique. X-ray diffraction analysis indicated the formation of a single-phase cubic structure with lattice parameter: a = (4.1158 ± 0.0003) Å. The synthesized powder was characterized using X-ray diffraction (XRD) scanning electron micrographs, energy dispersive X-ray analysis, differential thermal analysis, thermogravimetric analysis and Fourier transform infrared techniques. Electrical properties were studied using a.c. impedance spectroscopy technique in the temperature range of 50-650 °C and frequency range of 10 Hz-13 MHz. The complex impedance plots at temperature ≥300 °C show that total impedance is due to the contributions of grains, grain boundaries and electrode. Resistance of these contributions has been determined. Variation of these resistances with temperature shows the presence of two different regions with different slopes. The nature of variation for the above three resistances, in both the temperature regions confirms that conducting species (phases) responsible for grain, grain boundaries and electrode are the same. Based on the value of activation energy, it is proposed that conduction via hopping of doubly ionized oxygen vacancies (V••o) is taking place in the temperature region of 300-450 °C, whereas in the temperature region of 450-650 °C, hopping of proton, i.e. OH• ions occurs.