New Lead-free (1−x)BaTiO3–xBi(Mg1/2Zr1/2)O3 Solid Solution with Morphotropic Phase Boundary and Diffuse Phase Transition

Abstract

A new lead-free perovskite solid solution (1−x)BaTiO3–xBi(Mg1/2Zr1/2)O3 with morphotropic phase boundary (MPB) has been developed, and its structural and dielectric properties have been investigated. Rietveld structural analysis of the X-ray diffraction data suggest a composition-dependent tetragonal (P4mm) to cubic (Pm3m) phase transition with an intermediate, phase coexistence region, demarcating the MPB. The compositions with x ≤ 0.05 are tetragonal in the P4mm space group and the compositions with x ≥ 0.25 are cubic in the space group. Coexistence of monoclinic phase (space group Cm) with tetragonal/cubic phase (space group P4mm/ (Pm3m)) is observed in the MPB region for the compositions with 0.10 ≤ x ≤ 0.22. The temperature dependence of permittivity exhibits a nonrelaxor type diffuse phase transition for all the compositions across the MPB. © 2016 The American Ceramic Society