Residual strength of aluminum-lithium alloy center surface crack tension specimens at cryogenic temperatures

dc.contributor.author	Govindan Potti P.K.; Nageswara Rao B.; Srivastava V.K.
dc.date.accessioned	2025-05-24T09:56:26Z
dc.description.abstract	A three parameter fracture criterion which correlates the stress and the stress intensity factor at failure, is followed for the residual or fracture strength estimations of cracked configurations made of aluminum-lithium (Al-Li) alloys. The three fracture parameters are determined from the fracture data of Al-Li alloy center surface crack tension (SCT) specimens at cryogenic temperatures. It is found that the estimated fracture strength values compare well with the test results. © 2001 Elsevier Science Ltd. All rights reserved.
dc.identifier.doi	https://doi.org/10.1016/S0011-2275(01)00030-3
dc.identifier.uri	http://172.23.0.11:4000/handle/123456789/21019
dc.relation.ispartofseries	Cryogenics
dc.title	Residual strength of aluminum-lithium alloy center surface crack tension specimens at cryogenic temperatures